105℃ Modified Irradiation-Crosslinkable Polyethylene Insulation Compound

105℃ Modified Irradiation-Crosslinkable Polyethylene Insulation Compound

105℃ Modified Irradiation-Crosslinkable Polyethylene Insulation Compound is formulated with modified polyethylene resin as the base material, combined with various additives. This material features excellent stability and superior crack resistance, making it suitable for extrusion processing of both large and small cross-section power cables and control cables.

105℃ Modified Irradiation-Crosslinkable Polyethylene Insulation Compound List

Model	Unit	205E
Item	/	Typical
Density	g/cm3	0.93
Tensile Strength	MPa	18.6
Elongation at Break	%	650
Air Oven Aging	℃×h	135×168
Tensile Strength Change Rate	%	-10
Elongation at Break Change Rate	%	-11
Hot Set (0.2MPa)	℃×min	200×15
Elongation under Load	%	50
Permanent Deformation after Cooling	%	0
Low-temperature Performance Test	℃	-50
Low-temperature Impact Brittleness Temperature	℃	-76
Ozone Resistance Test	/	No cracking
4-hour AC Voltage Withstand Test	kV	/
Volume Resistivity at 20°C	Ω·cm	5.0×1015
Dielectric Strength at 20°C	kV/mm	29
Environmental Protection Requirements	/	Conforms to EU RoHS Directive (2011/65/EU) and REACH Regulation (EC 1907/2006) Substances of Very High Concern (SVHC) provisions.

105℃ Modified Irradiation-Crosslinkable Polyethylene Insulation Compound Application

105℃ Modified Irradiation-Crosslinkable Polyethylene Insulation Compound features excellent stability and superior crack resistance. It is suitable for the following applications:
1. Power cables;
2. Control cables.